- Solvay TECHNYL® C 216 V30 PA6, 30% glass fiber, DRY
Solvay TECHNYL® C 216 V30 PA6, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 216 V30 PA6, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced with 30 % of glass fiber, for injection molding.Available in: Asia Pacific and Latin AmericaProduct Applications: It has good mechanical properties, it is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. It is used in the automotive industry and electrical sectors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183/A |
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec |
0.95 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
| Elongation at Break | 3.8 % | 3.8 % | ISO 527 Type 1A |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 Type 1A |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75/Af |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Infiltrated Steel FX-227-T Powdered Metal
- Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated
- SABIC Innovative Plastics LNP Thermocomp FF004 PE
- Saint-Gobain COHRlastic® CF4420 High Heat Reinforced Solid Rubber
- Plenco 4311 Phenolic, Granular, Injection Molded
- Diamond Polymers ASA T-105
- Dow 560.00 Developmental Performance Polypropylene Polymer
- ChevronTexaco Cygnus® Grease NLGI Grade 1
- Axiall 9175 White 10 Rigid PVC, Molding, White 10
- Rochling Engineered Plastics Polystone® Reprocessed (UHMW-PE)
Copyright © lookpolymers.com All Rights Reserved