Firestone CG430-203 Nylon 6, 30% Fiberglass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Firestone |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Firestone CG430-203 Nylon 6, 30% Fiberglass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Natural color. Heat stabilized. Fiber size is 4 mm length and 14 µm diameter.Information provided by Firestone
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 156 MPa | 22600 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 7.78 GPa | 1130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C |
12.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Middle Barrel Temperature | 277 - 288 °C | 530 - 550 °F | |
| Front Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Nozzle Temperature | 260 - 271 °C | 500 - 520 °F | |
| Melt Temperature | 271 - 282 °C | 520 - 540 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % |
Users viewing this material also viewed the following:
- Nylene® 9110 Unfilled Nylon 6/10
- North Wood Plastics PS with 40% Wood Fiber
- Intercontinental Polymers CoPET 198 CoPET Polymer Type - Clear, Low Melt Polyester Pellets
- Guarniflon PTFE G455 Polytetrafluoroethylene 35% Carbographite
- Star Plastics PC/PBT7804 Molding Grade PC/PBT
- Sharadaa Ceramics Calcium Silicate Block
- Plastics Group Polifil® GFABS-30 30% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS)
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- Applied Composites 150 Polyester SMC
Copyright © lookpolymers.com All Rights Reserved