Solvay TECHNYL® A 60 G1 V30 PA66, 30% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 60 G1 V30 PA66, 30% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flame retardant Polyamide PA66 reinforced with 30% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This Red Phosphorous and Halogen free flame retardant grade, combines excellent all-round mechanical properties with outstanding flame retardancy (UL 5VA at 1.6mm) and electrical performance. This product is ideally suited for industrial controls and power distribution applications such as MCBs and contactors. The long term thermal performance of this grade also make it ideal for under-the-bonnet Auto applications where it can withstand temperatures of 160°C for over 6000hrs. This product is available in Natural, Grey and Black. Specific colors and Laser Marking grades optimized for YAG and UV laser types are also available upon request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183/A
Water Absorption 0.73 %

@Temperature 23.0 °C,
Time 86400 sec
 0.73 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
ISO 527 Type 1A
Elongation at Break 2.3 %
2.3 %
ISO 527 Type 1A
Tensile Modulus 11.7 GPa
1700 ksi
ISO 527 Type 1A
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.670 J/cm²
3.19 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO 75/Af
UL RTI, Electrical 145 °C

@Thickness 20000 mm
 293 °F

@Thickness 787 in
160 °C

@Thickness 6000 mm
 320 °F

@Thickness 236 in
UL RTI, Mechanical with Impact 140 °C

@Time 7.20e+7 sec
 284 °F

@Time 20000 hour
160 °C

@Time 2.16e+7 sec
 320 °F

@Time 6000 hour
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 1210
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 1210
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 1210
Oxygen Index 33 %
33 %
ISO 4589
Glow Wire Test 775 °C

@Thickness 0.800 mm
 1430 °F

@Thickness 0.0315 in
 ignition temperature; ISO 60695-2-13
775 °C

@Thickness 1.60 mm
 1430 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 260 - 275 °C
500 - 527 °F
Front Barrel Temperature 280 - 285 °C
536 - 545 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 275-280°C