Eurostar Staramide PB00A PA6, 50% Glass Bead Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PB00A PA6, 50% Glass Bead Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide PB00A is a 50% Glass Bead Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % @Temperature 23.0 °C, Time 86400 sec |
1.6 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 4.00 mm |
0.011 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 3.4 % | 3.4 % | Flexural, 2 mm/min; ISO 178 | |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |
| Zone 3 | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC1800R PC (Asia Pacific)
- Lucite International Lucite® 6751 Acrylic Bead Resin
- Teknor Apex Sinpolene MBB3331/A Low Density Polyethylene
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR MBT
- ExxonMobil Jayflex™ 220 Aliphatic Hydrocarbon Plasticizer
- Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
- Diamond Polymers ASA S130
- Axiall 19940 Wire & Cable Flexible PVC
- Asahi Kasei Thermylene® P6-25FG-0687 25% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved