PolyOne Edgetek® PE-30MC-20TC/000 High Density Polyethylene (HDPE), Talc Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PE-30MC-20TC/000 High Density Polyethylene (HDPE), Talc Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Mica FilledTalc FilledInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.427 g/cc | 1.427 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Thickness 3.17 mm |
0.010 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 1.59 GPa | 230 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 26.9 MPa | 3900 psi | ASTM D790 |
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
Users viewing this material also viewed the following:
- Resin Technology Group 388 Metals, Small Gap Fill Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- Garlock GRAPH-LOCK® 3125TC Graphite Sheet Gasketing, Steel Insert
- Indium Corp. Indalloy 191 Aluminum Solder Alloy
- LG Chemical LUPOL GP3202 PP+MF20%
- Momentive Performance Materials RTV6808 Translucent Industrial Plastic Adhesive/Sealant
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
- Master Bond Mastersil 410 One Component Room Temperature Curing Silicon
- DuPont Performance Polymers Delrin® 100AL NC010 Acetal (POM) (Unverified Data**)
- Buckeye Polymers BP FLEX A6310 NAT Thermoplastic Elastomer SEBS
- Channel Industries 300 Barium Titanate Piezoelectric
Copyright © lookpolymers.com All Rights Reserved