Material Notes:
BK-STAT Compounds are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanliness requirements in comparison to other materials based on Hygroscopic Antistats, Inherently Conductive Polymer Coating, or Conductive Fillers such as carbon fibers and carbon blacks.BK-STAT Compounds exhibit superior property and processing characteristics compared with other competitive IDP based compounds.Special Features:Superior Permanent Static DissipationExcellent Wear ResistanceHumidity InsensitivityExceptionally High Impact ResistanceNo Particle GenerationExcellent ProcessibilityApplications:Semiconductor PackagingLCD PackagingElectrical & ElectronicsMedical DevicesStorage DisksAppliancesConsumer GoodsClean Room Accessories
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 0.880 GPa | 128 ksi | ASTM D790 |
| Izod Impact, Notched | 1.90 J/cm | 3.56 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
| Static Decay | <= 0.50 sec | <= 0.50 sec | 5kV to 50V; FTMS 101C |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 °C | 140 - 158 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- MarkeTech Repton 314 Mullite
- Sumitomo Bakelite Durez® 153 Phenolic, Injection Grade
- SABIC Innovative Plastics LNP STAT-LOY M3000C PP
- Master Bond Mastersil 718 Adhesion Enhancement Silicone Primer
- Plenco 08133 Polyester BMC, Compression Molded
- Constellium Fortal® Aluminum Alloy
- Dow Corning SILASTIC® T-4 RTV SILICONE RUBBER BASE & T-4 O CURING AGENT
- Clariant Renol 6608G43 Nylon 66, 43% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- Beijing Ranger Chem PBT 403 M-G30 HF Halogen Free Flame Retarding FR PBT
- Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved