Solvay TECHNYLÂ® 2912GMH7-P PA66, 63% glass fiber, DRY

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer	Solvay
Trade Name	Technyl®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay TECHNYLÂ® 2912GMH7-P PA66, 63% glass fiber, DRY.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Polyamide 66, reinforced with 63% of glass fiber for injection molding.Available in: Asia PacificProduct Applications: TECHNYLÂ® 2912GMH7-P is used in all sectors of industry, offering excellent combination between mechanical properties and surface aspect. This grade is widely used for automotive part: outside mirror base plate. This product is available in black color and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.

Physical Properties	Metric	English	Comments
Density	1.72 g/cc	0.0621 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0025 cm/cm	0.0025 in/in
Linear Mold Shrinkage, Transverse	0.0045 cm/cm	0.0045 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	215 MPa	31200 psi	ASTM D638
Elongation at Break	1.5 %	1.5 %	ASTM D638
Flexural Strength	310 MPa	45000 psi	ASTM D790
Flexural Modulus	17.0 GPa	2470 ksi	ASTM D790
Izod Impact, Notched	2.15 J/cm	4.03 ft-lb/in	ASTM D265

Thermal Properties	Metric	English	Comments
Melting Point	262 Â°C	504 Â°F	ISO 11357
Deflection Temperature at 1.8 MPa (264 psi)	220 Â°C	428 Â°F	ASTM D648
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Processing Properties	Metric	English
Feed Temperature	260 - 265 Â°C	500 - 509 Â°F
Front Barrel Temperature	280 - 290 Â°C	536 - 554 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	80.0 Â°C	176 Â°F
Moisture Content	<= 0.20 %	<= 0.20 %

Descriptive Properties	Value	Comments
Compression Zone	265-275Â°C