Solvay TECHNYL® 27010ST PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® 27010ST PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, with very high impact resistance even at low temperature, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® 2710ST is used in all sector of industry, offering an excellent productivity. This grade is widely used for: Sports and leisure applications for shoe soles, ski components, ski and surf bindings; Toy applications, such as, the bumper of a remote-controlled car and Battery gaskets, Fastener. This product is available in available in natural, black and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Water Absorption | 1.05 % @Temperature 23.0 °C, Time 86400 sec |
1.05 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D786 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Izod Impact, Notched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D265 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.6 µm/m-°C @Temperature 23.0 - 85.0 °C |
7.00 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM D696 |
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ISO 1210 |
| Oxygen Index | 24.5 % | 24.5 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.2 | 3.2 | IEC60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution B; IEC 60112 |
| 575 V | 575 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 270 °C | 509 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Prodways PLASTCure ABS 3650 3D Printing Polymer
- Parker Chomerics CHO-BOND 1056, Part A Conductive Powder
- ACC QSil 30 QSI Quantum Silicones 50 Durometer Condensation Cure for Potting (discontinued **)
- Kobe Steel KS6-2-4-2 Alpha Titanium Alloy, AMS 4976, Solution treated and aged
- LG Chemical PI641 ABS, High Impact
- Lubrizol Estane® AG 8451 Thermoplastic Polyurethane
- Borealis Daplen™ ED213AE TPO Compound
- Braskem CP 405XP Compression Molding Polypropylene Heterophasic Copolymer
- Alliance S-26H Samarium Cobalt Magnetic Material
Copyright © lookpolymers.com All Rights Reserved