- Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY
Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamid 66, reinforced with 40% of glass fiber, heat stabilized for injection moldingAvailable in: Asia PacificProduct Applications: TECHNYL® 2412GHF8 is used in all sectors of industry. Offering excellent combination between thermal stability and mechanical properties. This grade is widely used for: Automotive parts-Pedal, oil filter hosing, cultch master cylinder. This product is available in black color and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 205 MPa | 29700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 305 MPa | 44200 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | ASTM D265 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.60 µm/m-°C @Temperature 23.0 - 85.0 °C |
2.00 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 270 °C | 509 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Plenco 50045 PET, Pellet, Injection Molded, White (discontinued **)
- LG Chemical LUPOY GP1000MR PC, Transparent
- Solvay TECHNYL® A 218 V15 PA66, 15% glass fiber, DRY
- Taiwan Sheen Soon Sheenthane® AS-626SH TPU for PU Adhesive
- SABIC Innovative Plastics LNP Thermocomp LC006E PEEK
- Solvay TECHNYL® C 536XT PA6, DRY
- Clariant Renol BR2084 Nylon 66, 33% Glass Fiber, PTFE Lubricated
- Chem Polymer Chemlon 225 G Nylon 6, 25% Glass Fiber Reinforced
- Ashley Polymers Ashlene® R6043 Nylon 6
- ExxonMobil Coolant/Antifreeze Mobil Heavy Duty
Copyright © lookpolymers.com All Rights Reserved