Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Glass Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.45 g/cc
0.0415 - 0.0524 lb/in³
Average value: 1.27 g/cc Grade Count:18
Water Absorption 0.0600 - 0.100 %
0.0600 - 0.100 %
Average value: 0.0922 % Grade Count:9
Moisture Absorption at Equilibrium 0.00600 - 0.0600 %
0.00600 - 0.0600 %
Average value: 0.0240 % Grade Count:3
Water Absorption at Saturation 0.200 - 0.220 %
0.200 - 0.220 %
Average value: 0.205 % Grade Count:4
Linear Mold Shrinkage 0.00100 - 0.00500 cm/cm
0.00100 - 0.00500 in/in
Average value: 0.00356 cm/cm Grade Count:16
Linear Mold Shrinkage, Transverse 0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
Average value: 0.00450 cm/cm Grade Count:4
Melt Flow 5.00 - 21.0 g/10 min
5.00 - 21.0 g/10 min
Average value: 15.0 g/10 min Grade Count:10
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 60.0 - 120 MPa
8700 - 17400 psi
Average value: 89.8 MPa Grade Count:13
Tensile Strength, Yield 50.0 - 110 MPa
7250 - 16000 psi
Average value: 82.9 MPa Grade Count:6
Elongation at Break 1.70 - 10.0 %
1.70 - 10.0 %
Average value: 5.01 % Grade Count:17
Modulus of Elasticity 3.80 - 10.6 GPa
551 - 1540 ksi
Average value: 6.83 GPa Grade Count:4
Flexural Yield Strength 80.0 - 190 MPa
11600 - 27600 psi
Average value: 133 MPa Grade Count:18
Flexural Modulus 3.00 - 10.0 GPa
435 - 1450 ksi
Average value: 5.60 GPa Grade Count:18
Izod Impact, Notched 0.641 - 1.23 J/cm
1.20 - 2.30 ft-lb/in
Average value: 0.894 J/cm Grade Count:8
0.694 - 0.694 J/cm

@Temperature -40.0 - -40.0 °C
1.30 - 1.30 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.694 J/cm Grade Count:1
Izod Impact, Unnotched 3.36 - 5.34 J/cm
6.29 - 10.0 ft-lb/in
Average value: 4.04 J/cm Grade Count:5
Izod Impact, Notched (ISO) 7.00 - 15.0 kJ/m²
3.33 - 7.14 ft-lb/in²
Average value: 12.5 kJ/m² Grade Count:11
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 106 - 145 °C
223 - 293 °F
Average value: 128 °C Grade Count:17
UL RTI, Electrical 50.0 - 110 °C
122 - 230 °F
Average value: 90.0 °C Grade Count:3
UL RTI, Mechanical with Impact 50.0 - 105 °C
122 - 221 °F
Average value: 86.7 °C Grade Count:3
UL RTI, Mechanical without Impact 50.0 - 110 °C
122 - 230 °F
Average value: 90.0 °C Grade Count:3
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:6
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+17 ohm-cm
1.00e+15 - 1.00e+17 ohm-cm
Average value: 2.08e+16 ohm-cm Grade Count:5
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
Average value: 1.00e+15 ohm Grade Count:3
Dielectric Strength 16.5 - 18.0 kV/mm
420 - 457 kV/in
Average value: 17.6 kV/mm Grade Count:4
Processing Properties Metric English Comments
Nozzle Temperature 277 - 316 °C
531 - 601 °F
Average value: 297 °C Grade Count:3
Melt Temperature 243 - 316 °C
469 - 601 °F
Average value: 290 °C Grade Count:7
Mold Temperature 71.1 - 107 °C
160 - 225 °F
Average value: 91.2 °C Grade Count:7
Drying Temperature 104 - 121 °C
219 - 250 °F
Average value: 115 °C Grade Count:7
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:3