Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins especially after exposure to humid environments. These materials were specifically designed for automotive electrical and electronic applications such as connectors, sockets, and sensors. Additional applications include fuel systems where both the high elongation/ductility and superior low permeation performance to automotive fuels are needed. They can be processed readily using conventional injection molding equipment and methods.Information provided by Solvay Advanced Polymers
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ISO 1183A
1.10 g/cc
1.10 g/cc
ASTM D792
Moisture Absorption at Equilibrium 0.50 %
0.50 %
24 hours; ASTM D570
Linear Mold Shrinkage 0.020 cm/cm
0.020 in/in
93°C; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
ISO 527
61.0 MPa
8850 psi
ASTM D638
Elongation at Break 15 %
15 %
ISO 527
Elongation at Yield 5.0 %
5.0 %
ISO 527
30 %
30 %
ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
ASTM D638
2.30 GPa
334 ksi
ISO 527
0.500 GPa

@Temperature 100 °C
72.5 ksi

@Temperature 212 °F
ISO 527
Flexural Strength 65.0 MPa
9430 psi
ISO 178
92.0 MPa
13300 psi
ASTM D790
9.00 MPa

@Temperature 100 °C
1310 psi

@Temperature 212 °F
ISO 178
Flexural Modulus 1.80 GPa
261 ksi
ISO 178
2.10 GPa
305 ksi
ASTM D790
0.400 GPa

@Temperature 100 °C
58.0 ksi

@Temperature 212 °F
ISO 178
Shear Strength 53.0 MPa
7690 psi
ASTM D732
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched NB
NB
ISO 179/1eA
Dynatup @ -18°C 54.0 J
39.8 ft-lb
Total Energy. Dry as molded. No temperature indicated.; D3763
Dynatup @ -18°C Max Load 454000 g
1000 lb
No temperature indicated.; D3763
Thermal Properties Metric English Comments
CTE, linear 94.0 µm/m-°C

@Temperature 0.000 - 800 °C
52.2 µin/in-°F

@Temperature 32.0 - 1470 °F
Melting Point 300 °C
572 °F
ISO 11357-3
300 °C
572 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
ISO 75Af
185 °C
365 °F
ASTM D648
Flammability, UL94 HB
HB
Shrinkage 1.9 %
1.9 %
Electrical Properties Metric English Comments
Volume Resistivity 3.90e+15 ohm-cm
3.90e+15 ohm-cm
ASTM D257
Surface Resistance 3.80e+15 ohm
3.80e+15 ohm
ASTM D257
Dielectric Constant 3.2

@Frequency 60 Hz
3.2

@Frequency 60 Hz
ASTM D150
3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 17.0 kV/mm
432 kV/in
ASTM D149
Dissipation Factor 0.0040

@Frequency 60 Hz
0.0040

@Frequency 60 Hz
ASTM D150
0.016

@Frequency 1e+6 Hz
0.016

@Frequency 1e+6 Hz
ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
ASTM D3638
High Voltage Arc-Tracking Rate, HVTR 4.20 mm/min
0.165 in/min
UL 746A