Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: slippers, inserts for coupling boxes, wear linersInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | DIN 53473 |
| Water Absorption at Saturation | 4.0 % @Temperature 20.0 °C |
4.0 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 110 MPa | 16000 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO-DIS 527 |
| Creep Strength | >= 8.00 MPa | >= 1160 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 12.0 MPa | >= 1740 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | DIN 53457 |
| Flexural Strength | 50.0 MPa | 7250 psi | DIN 54352 |
| Flexural Modulus | 2.10 GPa | 305 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | >= 18.0 kJ/m² | >= 8.57 ft-lb/in² | ISO 180-1A |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.080 | 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.30 | >= 0.30 | ISO-DIS 527 |
| K Factor (Wear Factor) | 6.00e-11 | 6.00e-11 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 200 - 220 °C | 392 - 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.030 | 0.030 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3b | DIN 53480 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics EXTEM XH1015 TPI Resin
- Precision Polymer Engineering C90B Chloroprene Rubber
- PolyOne Edgetek® AS-10GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- Karina E900D10/1-E-IS-BZ White PVC Compound
- Lubriplate FMO 900 AW USP Mineral Oil-Based Food Machinery Grade Oil
- Teknor Apex Monprene® MP-1644L3 Thermoplastic Elastomer
- Dow Corning LSPYW31 SILICONE MASTERBATCH YELLOW
- CP-Polymer-Technik Wellamid® 6000 MR 409 HWCP Mineral Nylon 6, Heat Stabilized, Dry
- Eurotec® Tecomid® NA40 MR15 NL IL PA6.6, 15% mineral filled, impact modified, natural
- ArcelorMittal HSLA 340 High strength low alloy steel for cold forming, Cold Rolled
Copyright © lookpolymers.com All Rights Reserved