LyondellBasell Pro-faxâ„¢ SG899 Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | LyondellBasell |
| Trade Name | Pro-fax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Pro-faxâ„¢ SG899 Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Pro-faxâ„¢ SG899 high flow, high impact polypropylene copolymer resin is tailored for use in automotive interior head impact applications. This resin is designed to be run in conventional injection molding equipment using standard polypropylene processing conditions. It is available in pellet form. All ingredients in Pro-faxâ„¢ SG899 resin meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: Automotive interior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 & ISO 1183 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | ASTM D 638 |
| 22.0 MPa | 3190 psi | ISO 527-1, -2 | |
| Elongation at Break | 50 % | 50 % | ISO 527-1, -2 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1, -2 |
| 6.0 % | 6.0 % | ASTM D 638 | |
| Flexural Modulus | 1.03 GPa | 150 ksi | 1% Secant, 0.05 in/min; ASTM D790 |
| 1.10 GPa | 160 ksi | ISO 178 | |
| Izod Impact, Notched | 2.99 J/cm | 5.60 ft-lb/in | 73°F; ASTM D256 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature -40.0 °C |
2.62 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 7.50 kJ/m² @Temperature -18.0 °C |
3.57 ft-lb/in² @Temperature -0.400 °F |
ISO 180 | |
| 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | Unannealed; ISO 75B-1, -2 |
| 97.8 °C | 208 °F | Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | Unannealed; ISO 75A-1, -2 |
Users viewing this material also viewed the following:
- 3M Dyneon™ TF 4246 PTFE 35% Electrocarbon Filled (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-1330 PEEK, with PTFE
- Solvay Specialty Polymers Polymist® XPP 515-S Polytetrafluoroethylene (PTFE)
- Silon Taborex TA 1108 HD Chemically-Crosslinkable HDPE Compound
- A. Schulman PP 984 Polypropylene Medium Impact Polypropylene
- CP-Polymer-Technik Wellamid® 6000/505 GS 30 HWCP 30% Impact Modified Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- C.O.I.M. PLAXTER® P 90 Polymeric Plasticizer
- Applied Composites 150 Polyester SMC
Copyright © lookpolymers.com All Rights Reserved