- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene
Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 320U is an UV protected, high impact resistant and easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 42.0 MPa | 6090 psi | ISO 527-1 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-1 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| 100 kJ/m² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.40 J/cm² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 95.0 °C @Thickness 2.00 mm |
203 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 95.0 °C | 203 °F | 50B; ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1820L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Niagara LaSalle 8620 Leaded Cold Finished Steel Bar
- Abatron 85082 A/B Filled Potting Compound (discontinued **)
- A. Schulman POLYFORT™ FPP 3707 CAC03 Filled Homopolymer Polypropylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N220 Filler
- BASF Ultramid® 66 H2 G/25-V0KB1 BK 3324 PA66 (Dry)
- Adell BJ-13 Nylon 6, 15% Glass Reinforced; High Impact
- 3M FM057 Indoor UL Recognized Brite Silver Polyester Label Products
- BASF Paliogen® Red L 3880 HD Color Additive
- Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved