Sax Polymers SAXATEC 6120 AES
| Category | Polymer , Thermoplastic , AES Polymer |
| Manufacturer | Sax Polymers |
| Trade Name | SAXATEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXATEC 6120 AES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXATEC 6120 is a easy lowing, weatherable AES injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 21 g/10 min @Load 10.0 kg, Temperature 220 °C |
21 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 37.0 MPa | 5370 psi | ISO 527-1 |
| Elongation at Break | 30 % | 30 % | ISO 527-1 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 3.20 J/cm² @Temperature 23.0 °C |
15.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 80.0 °C @Thickness 2.00 mm |
176 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 94.0 °C | 201 °F | 50B; ISO 306 |
| Glow Wire Test | 650 °C | 1200 °F | IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs EU410 EuCl3·6H2O Europium(III) chloride hexahydrate
- Precision Polymer Engineering Q70X Polyurethane Rubber
- Raschig Group 2557 AMC Polyester
- SABIC Innovative Plastics Lexan® HP6NR PC (Europe-Africa-Middle East)
- PolyOne Geon™ Specialty Suspension Impel S100 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- LyondellBasell Ethanol, 200 Proof
- MMCC Aluminum/Graphite Fiber GA 7-230 Metal Matrix Composite
- Solvay SOPROPHOR® 4 D 360 Surfactant
- Tra-Con Tra-Bond 216D02 Thixotropic No-Sag Epoxy Adhesive
- Shinkong Synthetic Fibers Shinite® PP4210 PP, Fire Retardant
Copyright © lookpolymers.com All Rights Reserved