- Sax Polymers SAXAMID 226 Nylon 6.6
Sax Polymers SAXAMID 226 Nylon 6.6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226 Nylon 6.6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226 is a general purpose polyamide 6.6 injection-molding-grade. Benefits are short cycle times and good release properties.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 85.0 MPa | 12300 psi | 50 mm/min; ISO 527-1 |
| Elongation at Break | 7.0 % | 7.0 % | 50 mm/min; ISO 527-1 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 245 °C | 473 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Udel® M-2300 MR Polysulfone (PSU), Mold Release (discontinued **)
- Lubriplate SYN LUBE 220 PAO-Based Multi-Purpose Synthetic Fluid
- Lucite International Colacryl ® TS 1672 Acrylic Orthodontic Polymer
- Shinkong Synthetic Fibers Shinite® N601G30 Nylon 66, 30% Glass Filled
- SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin
- Wellman Wellamid® MRT1487 BK Nylon 66, 32% Mineral Reinforced
- ExxonMobil 10W-30 Exxon XD-3
- Ametek P434L P/M Stainless Steel, Sintered from 7.0 g/cc Green Density
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 65A
Copyright © lookpolymers.com All Rights Reserved