BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Water Absorption 7.5 %
7.5 %
ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 30 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 103 MPa
14900 psi
0.2 in/min; ASTM Test
163 MPa

@Temperature -40.0 °C
 23600 psi

@Temperature -40.0 °F
 ISO Data
Tensile Strength, Ultimate 110 MPa
16000 psi
5mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa

@Temperature 80.0 °C
 7690 psi

@Temperature 176 °F
 ISO Data
Elongation at Break 4.0 %
4.0 %
5mm/min; ISO 527
4.0 %
4.0 %
0.2 in/min; ASTM Test
4.5 %

@Temperature -40.0 °C
 4.5 %

@Temperature -40.0 °F
 ISO Data
Elongation at Yield 8.6 %

@Temperature 80.0 °C
 8.6 %

@Temperature 176 °F
 ISO Data
Tensile Modulus 5.17 GPa
750 ksi
ASTM Test
5.50 GPa
798 ksi
1mm/min; ISO 527
Flexural Modulus 4.48 GPa
650 ksi
ASTM Test
4.50 GPa
653 ksi
ISO Data
Izod Impact, Notched 0.530 J/cm

@Temperature -40.0 °C
 0.993 ft-lb/in

@Temperature -40.0 °F
 ASTM Test
1.07 J/cm

@Thickness 3.17 mm
 2.00 ft-lb/in

@Thickness 0.125 in
 ASTM Test
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
ISO Test
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
ISO 179
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
ISO 179
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.0 µm/m-°C
18.3 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 75.0 µm/m-°C
41.7 µin/in-°F
ISO 11359
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ISO 75
204 °C
399 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
ISO 75
193 °C
379 °F
ASTM Test
Flammability, UL94 HB

@Thickness 1.62 mm
 HB

@Thickness 0.0638 in
HB

@Thickness 0.730 mm
 HB

@Thickness 0.0287 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.025

@Frequency 1.00e+6 Hz
 0.025

@Frequency 1.00e+6 Hz
 IEC 60250
0.025

@Frequency 100 Hz
 0.025

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 550 V
550 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified Yes
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat