Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % @Time 86400 sec |
0.70 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 240 MPa | 34800 psi | ISO 527-1/-2 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527-1/-2 |
| Tensile Modulus | 17.5 GPa | 2540 ksi | ISO 527-1/-2 |
| Flexural Strength | 380 MPa | 55100 psi | ISO 178 |
| Flexural Modulus | 16.8 GPa | 2440 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C | 12.2 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Dielectric Strength | 42.1 kV/mm @Thickness 1.00 mm |
1070 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_Grid_7523 Transparent Prototyping Polymer
- NOVA Chemicals Gedexcel® 45B Expandable Polystyrene
- SMAC CABLE® 2521S-40-08 Damping Material
- Supreme Petrochem SP 6410 0003 Abrasion Resistant Polystyrene
- Adell EZ-16 Homopolymer Polypropylene, 30% Calcium Carbonate Filled
- Beijing Evergrow Resources Nylon Activated Carbon
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer (discontinued **)
- LyondellBasell Hifax™ HSBMCB1158LS Thermoplastic Polyolefin Elastomer
Copyright © lookpolymers.com All Rights Reserved