Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527-1 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527-1 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 72.0 MPa | 10400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 21.0 kJ/m² @Temperature -30.0 °C |
9.99 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 2.10 J/cm² @Temperature -30.0 °C |
9.99 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 175 °C | 347 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs YB300 Yb2(CO3)3·xH2O Ytterbium carbonate hydrate
- Pearl Engineering PEPLPET B-101C PET Sheet Grade
- Solvay Specialty Polymers Aquivion® E87-05S Tetrafluoroethylene + SFVE (TFE+SFVE)
- SK Chemicals SKYTHANE® 155D R series Polyurethane
- A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene
- DSM Akulon® M-1016 (Dry) 33% Glass Reinforced Nylon 66 (North America)
- Dow 6D20 Polypropylene Random Copolymer Resin
- ATI Wah Chang Nb/Nb Alloy C-3009
- ExxonMobil Escorene® HDZ-123 HMW-HDPE Blown Film Resin (discontinued **)
- Loctite® Output™ 383 Acrylic Adhesive
Copyright © lookpolymers.com All Rights Reserved