Huntsman Rexell® H3108 Cast Film Extrusion LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman Rexell® H3108 Cast Film Extrusion LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Linear low density octene copolymerApplications: Cast film extrusionFilm properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.960 g/cc	0.0347 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	724 %	724 %	ASTM D882
Film Elongation at Break, TD	>= 769 %	>= 769 %	ASTM D882
Secant Modulus, MD	0.717 GPa	104 ksi	ASTM D882
Secant Modulus, TD	0.869 GPa	126 ksi	ASTM D882
Elmendorf Tear Strength MD	26 g	26 g	ASTM D1922
Elmendorf Tear Strength TD	358 g	358 g	ASTM D1922
Elmendorf Tear Strength, MD	1.02 g/micron	26.0 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	14.1 g/micron	358 g/mil	ASTM D1922
Dart Drop	1.93 g/micron	49.0 g/mil	ASTM D1709
Dart Drop Test	49.0 g	0.108 lb	ASTM D1709
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Film Tensile Strength at Break, TD	25.0 MPa	3630 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	21 %	21 %	ASTM D1003
Gloss	44 %	44 %	at 45°; ASTM D523