- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS
Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 42.7 MPa @Thickness 3.17 mm |
6200 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 17 % @Thickness 3.17 mm |
17 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 62.7 MPa @Thickness 3.17 mm |
9100 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.14 GPa @Thickness 3.17 mm |
310 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.49 J/cm @Thickness 3.17 mm |
2.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.35 mm |
230 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | Unannealed; ISO R 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| HB @Thickness 6.00 mm |
HB @Thickness 0.236 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.6 - 108 MPa | 9950 - 15600 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV Resistance | <1 Delta E | 300 Hr. Ivory Color; ASTM D4459 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CH200LN Polypropylene, Homopolymer, CR, Antistat, Nucleated, Injection Molding
- Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, Conditioned
- ExxonMobil 80W-90 Mobilube HD LS
- 3M FP024900 White Polypropylene Label Products
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-550 (FEF)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N220 (ISAF) Filler
- Industeel SUPERELSO® 890 HLE Steel for Welded and Weight-Saving Structures
Copyright © lookpolymers.com All Rights Reserved