- Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS
Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 40.7 MPa | 5900 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 58.6 MPa | 8500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.05 GPa | 298 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.11 J/cm @Thickness 3.17 mm |
7.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm |
185 °F @Thickness 0.250 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | 5 kg; 50°C/hr; ISO R 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.6 - 108 MPa | 9950 - 15600 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- ExxonMobil LL 3301.63 Premium High Strength Film Resin (discontinued **)
- Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 17 lb
- Shin-Etsu Silicones KE-971U Silicone Elastomer
- SABIC Innovative Plastics NORYL N190X PPE+PS
- Polyram RamTough PZ307G4 Polycarbonate, 20% Glass Fiber, UV Stabilized
- Eagle Brass 230 Red Brass, 3/4 Hard
- Dow R7021-50RNA Polypropylene Random Copolymer Resin
- ConocoPhillips Tacna® M5 Grease NLGI Grade 2
- Wanhua Chemical Wanthane® WHT-1595 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved