Cossa Polimeri ESTACARB 1601 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTACARB
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTACARB 1601 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose polycarbonateHigh melt flow rate, high impact resistanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ASTM D 638
Tensile Strength, Yield 62.0 MPa
8990 psi
ASTM D 638
Elongation at Break >= 50 %
>= 50 %
ASTM D 638
Flexural Modulus 2.50 GPa
363 ksi
ASTM D 790
Izod Impact, Notched 5.00 J/cm

@Temperature 0.000 °C
 9.37 ft-lb/in

@Temperature 32.0 °F
 ASTM D 638
6.00 J/cm

@Temperature 23.0 °C
 11.2 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Thermal Properties Metric English Comments
Hot Ball Pressure Test 135 °C
275 °F
I.E.C. 335-1
Vicat Softening Point 144 °C

@Load 5.00 kg
 291 °F

@Load 11.0 lb
 50°C/hr; ASTM D 1525
150 °C

@Load 0.999 kg
 302 °F

@Load 2.20 lb
 50°C/hr; ASTM D 1525
Flammability, UL94 V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
Glow Wire Test 850 °C

@Thickness 2.00 mm
 1560 °F

@Thickness 0.0787 in
 I.E.C. 695-2-1