- Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact
Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 250 °C |
20 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength at Break | 47.1 MPa | 6830 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 55.9 MPa | 8110 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 47 % | 47 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.794 J/cm @Thickness 6.35 mm |
1.49 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.922 J/cm @Thickness 3.17 mm |
1.73 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C @Thickness 6.40 mm |
268 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 146 °C | 295 °F | B/50; ISO R306 |
| 148 °C | 298 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- Polimersan Plastics POLITEF® (PTFE) with 25% Carbon
- PolyOne Elastamax™ XL-2065 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability
- Akro-Plastic Akromid® S31 (3484) PA 6.10 Dry (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 310ºF Cure Temperature
- Eagle Brass 260 Cartridge Brass, 3/4 Hard
- Cossa Polimeri ESTABLEND 8500 Polycarbonate ABS Blend
- Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4"
- 3M Cushion-Mount™ 1120 Plus Plate Mounting Tape
Copyright © lookpolymers.com All Rights Reserved