- Samyang Triel® 5450 Thermoplastics Polyetherester Elastomer, General Extrusion
Samyang Triel® 5450 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5450 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5450 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.017 cm/cm | 0.015 - 0.017 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 11 g/10 min @Load 2.16 kg, Temperature 240 °C |
11 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 20.6 MPa | 2990 psi | ASTM D638 |
| Tensile Strength, Yield | 5.88 MPa @Strain 5.00 % |
853 psi @Strain 5.00 % |
ASTM D638 |
| 8.34 MPa @Strain 10.0 % |
1210 psi @Strain 10.0 % |
ASTM D638 | |
| 12.7 MPa @Strain 50.0 % |
1850 psi @Strain 50.0 % |
ASTM D638 | |
| Flexural Yield Strength | 5.39 MPa | 782 psi | ASTM D790 |
| Flexural Modulus | 0.0902 GPa | 13.1 ksi | ASTM D790 |
| Izod Impact, Notched | NB @Thickness 3.17 mm, Temperature -40.0 °C |
NB @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 °C | 410 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Vicat Softening Point | 161 °C | 322 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Parabeam Industrie Paraglass 8 3D Glass Fabric
- Parker Chomerics CHO-SHIELD® 4937 Part B Barrier Coating Component
- Plastcom SLOVASTER® C FRU 2 PBT, flame retarder
- ICO Polymers ICORENEâ„¢ 190-3561 LMDPE Rotational Molding Resin
- SABIC Innovative Plastics Ultem ATX100R PEI+PCE (Asia Pacific)
- Goodfellow Copper 56.4/Titanium 43.6 Alloy
- A. Schulman POLYBATCH™ Norwegian Wood 60242U/3 Concentrate Based In LLDPE
- Covestro Makrolon® FU1007 Polycarbonate
- Daikin NEOFLON AF-1150 PFA Film
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Manganese AL 201LN™, M-7 (UNS S20153)
Copyright © lookpolymers.com All Rights Reserved