PolyOne OnFlex™ U 5470A-E0083 Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	OnFlex™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne OnFlex™ U 5470A-E0083 Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OnFlex™-U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™-U 5400 series are based upon alloys of SEBS and aliphatic TPU, combining the advantages of both raw materials, for example the good processability and soft haptic of a TPE-S with the excellent mechanical properties and abrasion resistance of a TPE-U. OnFlex™-U 5400 compounds are formulated to deliver very good scratch resistance, a wide hardness range, good chemical resistance, and good light stability.Properties are measured using injection molded plaques.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70	70	ISO 868
Tensile Strength at Break	21.3 MPa @Thickness 2.00 mm, Temperature 23.0 °C	3090 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min Across Flow; ISO 37
	22.2 MPa @Thickness 2.00 mm, Temperature 23.0 °C	3220 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min; Flow; ISO 37
Elongation at Break	480 % @Thickness 2.00 mm, Temperature 23.0 °C	480 % @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min Across Flow; ISO 37
	490 % @Thickness 2.00 mm, Temperature 23.0 °C	490 % @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min; Flow; ISO 37
Tear Strength	56.0 kN/m @Thickness 2.00 mm, Temperature 23.0 °C	320 pli @Thickness 0.0787 in, Temperature 73.4 °F	Method A, Trouser, 500 mm/min Across Flow; ISO 34-1
	59.0 kN/m @Thickness 2.00 mm, Temperature 23.0 °C	337 pli @Thickness 0.0787 in, Temperature 73.4 °F	Method A, Trouser, 500 mm/min; Flow; ISO 34-1
Abrasion	35	35	[mm³]; DIN 53516

Processing Properties	Metric	English
Melt Temperature	160 - 200 °C	320 - 392 °F
Mold Temperature	30.0 - 60.0 °C	86.0 - 140 °F
Drying Temperature	100 °C	212 °F
Dry Time	2.00 hour	2.00 hour

Descriptive Properties	Value	Comments
Appearance	Matte Finish
Features	Good Abrasion Resistance
	Good UV Resistance
	Oil Resistant
	Scratch Resistant
Fogging	1.1 mg	DIN 75201B; 100°C
Forms	Pellets
Generic Material	TPE
Generic Material Type	Thermoplastic Polyurethane Elastomer Alloy (TPU Alloy)
Generic Name	Thermoplastic Elastomer (TPE)
Injection Rate	Slow
Manufacturer / Supplier	GLS Thermoplastic Elastomers
Odor rating	2.3	VDA 270
Processing Method	Calendering
	Film Extrusion
	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Consumer Applications
	General Purpose
	Industrial Applications
	Power/Other Tools