SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.14 %
0.14 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %

@Temperature 23.0 °C
0.16 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 265 °C
11 g/10 min

@Load 4.76 lb,
Temperature 509 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
50 mm/min; ISO 527
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D 638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 133 %
133 %
50 mm/min; ISO 527
135 %
135 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.8 %
5.8 %
50 mm/min; ISO 527
6.3 %
6.3 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.14 GPa
310 ksi
50 mm/min; ASTM D 638
2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.100 J/cm

@Temperature -30.0 °C
0.187 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
5.20 J/cm

@Temperature 23.0 °C
9.74 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 70.0 J

@Temperature 23.0 °C
51.6 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
104 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
104 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
106 °C

@Thickness 3.20 mm
223 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 124 °C
255 °F
Rate B/50; ISO 306
126 °C
259 °F
Rate B/120; ISO 306
126 °C
259 °F
Rate B/50; ASTM D 1525
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
2.0 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 86 %

@Thickness 2.54 mm
86 %

@Thickness 0.100 in
ASTM D 1003