SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ASTM D 792
1.38 g/cc
0.0499 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0095 cm/cm

@Time 86400 sec
0.0095 in/in

@Time 24.0 hour
ISO 294
0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D 955
0.011 cm/cm

@Time 86400 sec
0.011 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.0 MPa
10400 psi
ISO 527
73.0 MPa
10600 psi
ASTM D 638
Tensile Strength, Yield 73.0 MPa
10600 psi
ASTM D 638
73.0 MPa
10600 psi
ISO 527
Elongation at Break 7.6 %
7.6 %
ASTM D 638
8.8 %
8.8 %
ISO 527
Elongation at Yield 6.3 %
6.3 %
ASTM D 638
6.4 %
6.4 %
ISO 527
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D 638
Flexural Strength 96.0 MPa
13900 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D 790
2.40 GPa
348 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
0.993 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.39 J/cm

@Temperature 23.0 °C
10.1 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 36.0 kJ/m²

@Temperature 23.0 °C
17.1 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.28
0.28
ASTM D 3702 Modified
Coefficient of Friction, Static 0.18
0.18
ASTM D 3702 Modified
K (wear) Factor 94.7 x 10-8 mm³/N-M
47.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
49.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
50.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 203 °C
397 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
206 °C

@Thickness 3.20 mm
403 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 187 °C
369 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
187 °C

@Thickness 3.20 mm
369 °F

@Thickness 0.126 in
unannealed; ASTM D 648