SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Viscosity | 210000 cP | 210000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.20 mm |
0.012 - 0.016 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
10 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D638 |
| 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| 150 % | 150 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 5 mm/min; ASTM D638 |
| 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 43.0 MPa | 6240 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| 7.50 J/cm @Temperature -30.0 °C |
14.1 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 7.00 J/cm² | 33.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 100 J @Temperature 23.0 °C |
73.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 100 J | 73.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| 130 µm/m-°C @Temperature 23.0 - 60.0 °C |
72.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature -40.0 - 40.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 117 °C | 243 °F | Rate B/50; ASTM D1525 |
| 117 °C | 243 °F | Rate B/50; ISO 306 | |
| 120 °C | 248 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Oceanchem Group Ammonium Bromide Photo Grade II
- Nilit FRIANYL A63 HH-FK 1020 Nylon 6.6 for injection molding, 10% glass fiber and 20% glass ball reinforced
- PolyOne Geon™ 170 Series 171 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Nilit Nilamid B3 H ZA Unfilled, Low Temperature Impact Resistant PA6
- Shin-Etsu Silicones KE-3494 Silicone, RTV
- Covestro Texin® 990 Urethane Thermoplastic Elastomer
- 3M Scotch-Weld™ CA100 Instant Adhesive
- Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester
- Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved