SABIC Innovative Plastics Valox® 830F PBT+PET (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 830F PBT+PET (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Physical Properties Metric English Comments
Specific Gravity 1.54 g/cc
1.54 g/cc
ASTM D792
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH
0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.15 %
0.15 %
ASTM D570
0.15 %
0.15 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 18 g/10 min

@Load 2.16 kg,
Temperature 265 °C
18 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 260 °C
13 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
2.5 %
2.5 %
5 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 8.00 GPa
1160 ksi
5 mm/min; ASTM D638
9.00 GPa
1310 ksi
1 mm/min; ISO 527
Flexural Yield Strength 170 MPa
24700 psi
1.3 mm/min, 50 mm span; ASTM D790
200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Modulus 7.00 GPa
1020 ksi
1.3 mm/min, 50 mm span; ASTM D790
8.00 GPa
1160 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
0.700 J/cm

@Temperature -30.0 °C
1.31 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
13.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
81.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
45.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
195 °C

@Thickness 3.20 mm
383 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 200 °C
392 °F
Rate B/50; ASTM D1525
200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306