SABIC Innovative Plastics LNP LUBRILOY DX08333 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY DX08333 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Lubriloy* DX08333 is an internally lubricated compound based on Lexan* Polycarbonate resin. Added features of this material include: ESD Safe, PTFE-free Wear & Friction solution and balanced mechanical performance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm | 0.0035 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
| 113 MPa | 16400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 5 mm/min; ASTM D638 |
| 7.31 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
| 113 MPa | 16400 psi | ISO 178 | |
| Flexural Modulus | 6.10 GPa | 885 ksi | ASTM D790 |
| 6.76 GPa | 980 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.96 J/cm | 5.55 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| K (wear) Factor | 161 x 10-8 mm³/N-M | 80.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1.00e+6 ohm | 10 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 362HF (RL) Synthetic Oil
- Nye Lubricants 723K (RL) Rheolube Grease
- Nanocyl EPOCYL™ NC E128-02 Master Batch Liquid Bisphenol-A Resin for non-Solvent Based Formulation Purposes
- Victrex® PEEK -HT™ 22GL30 Polyetherketone, 30% Glass Fiber Reinforced
- Kingfa FRHIPS-960 Flame Retardant Polystyrene
- Michelman® DigiGuard® Gloss 100 Water based overprint varnish
- Fiberfil® J-60/20/E/HF Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled, improved flow
- Lubrizol ESTALOC® T5160 Ether-Type, Reinforced Engineering Thermoplastic (European Grade)
- IRPC Polimaxx Polene 2340S Polypropylene Block Copolymer
Copyright © lookpolymers.com All Rights Reserved