Ineos ABS Lustran® H605
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H605.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low emission, easy flowing.,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 220 °C |
26 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | |
| Vicat Softening Point | 101 °C | 214 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 120E Al(OH)3
- LG Chemical Lupox® GP-2151F General Purpose PBT, 15% Glass Fiber Reinforced, Flame Retardant
- Spartech PP5430 Glass Fiber Reinforced Homopolymer
- A. Schulman POLYBATCH™ U-7025-CFK Blowing Agent Concentrate Based In Polystyrene
- A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- DSM Biomedical Elasthane™ 75D Thermoplastic Polyether Polyurethane (TPU)
- ATI Allvac® REX 734™ UNS S31675 Specialty Steel
- Karina E 57/200-D-AT-IS-SI-SD Clear PVC Compound
Copyright © lookpolymers.com All Rights Reserved