SABIC Innovative Plastics Valox® 365 PET (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 365 PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"".
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 0.750 - 2.30 mm |
0.0080 - 0.011 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.010 - 0.014 cm/cm @Thickness 2.30 - 4.60 mm |
0.010 - 0.014 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.013 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.012 - 0.016 cm/cm @Thickness 2.30 - 4.60 mm |
0.012 - 0.016 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 1.70 J/cm @Temperature -40.0 °C |
3.18 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 1.92 J/cm @Temperature -30.0 °C |
3.60 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Gardner Impact | 37.0 J | 27.3 ft-lb | ASTM D3029 |
| 37.0 J | 27.3 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 79.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| 82.8 µm/m-°C @Temperature 60.0 - 138 °C |
46.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C @Thickness 6.40 mm |
264 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm |
V-0 @Thickness 0.0299 in |
UL 94 |
| 5VA @Thickness 2.20 mm |
5VA @Thickness 0.0866 in |
UL 94 | |
| Oxygen Index | 28.8 % | 28.8 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 5.7 @Frequency 1.00e+6 Hz |
5.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 8.5 @Frequency 100 Hz |
8.5 @Frequency 100 Hz |
ASTM D150 | |
| Dielectric Strength | 12.0 kV/mm @Thickness 3.20 mm |
305 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
ASTM D150 |
| 0.030 @Frequency 1.00e+6 Hz |
0.030 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.75cm^3/g | ASTM D792 |
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following:
- MV Labs RB1000 Rb2SO4 Rubidium sulfate
- SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer
- Teknor Apex APEX® 94-A0098A-75 Polyvinyl Chloride, Flexible
- Solvay ALKAMIDE® AK50BN Surfactant
- Polyram Polytron P40B07 Polypropylene, 40% Long Glass Fiber, UV Stabilized
- Hexcel® HexForce™ 388 Aramid Fabric
- Dow Corning XIAMETER® PMCPPMX-200, 0.65CS Silicone Fluid
- Dymax 3070 Solvent-Free Plastic Adhesive
- Arkema Group Rilsan® AMN Y TLD Nylon 12, MoS2 Filled (Dry)
- EG72D Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved