Outokumpu 4762 High Temperature Ferritic Stainless Steel

Category	Metal , Ferrous Metal , Ferritic , Stainless Steel
Manufacturer	Outokumpu
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Outokumpu 4762 High Temperature Ferritic Stainless Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Highest chromium content-most resistant to reducing sulphurous gases. Susceptible to 475°C embrittlement and s-phase forms during long exposures in the range 600-800°C.Applications: Mostly used in high temperature applications with sulphurous atmospheres and/or low tensile loads such as for installations within: Chemical industry (drums)Power industry (coal burners)Metalworking industry (heat treatment boxes)Furnace technology (walls, doors)Available in hot rolled plate (Quarto) form.

Physical Properties	Metric	English	Comments
Density	7.50 g/cc	0.271 lb/in³	RT

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	223	223	RT; EN 10003-1
Tensile Strength, Ultimate	555 MPa	80500 psi	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Tensile Strength, Yield	405 MPa @Strain 0.200 %	58700 psi @Strain 0.200 %	Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
	440 MPa @Strain 1.00 %	63800 psi @Strain 1.00 %	Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
Elongation at Break	30 %	30 %	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1

Thermal Properties	Metric	English	Comments
CTE, linear	12.0 µm/m-°C @Temperature 600 °C	6.67 µin/in-°F @Temperature 1110 °F
	12.9 µm/m-°C @Temperature 800 °C	7.17 µin/in-°F @Temperature 1470 °F
	14.0 µm/m-°C @Temperature 1000 °C	7.78 µin/in-°F @Temperature 1830 °F
Specific Heat Capacity	0.460 J/g-°C	0.110 BTU/lb-°F	RT
Thermal Conductivity	14.2 W/m-K	98.5 BTU-in/hr-ft²-°F	RT
	20.9 W/m-K @Temperature 500 °C	145 BTU-in/hr-ft²-°F @Temperature 932 °F
Maximum Service Temperature, Air	1150 °C	2100 °F	Dry Air

Component Elements Properties	Metric	English
Aluminum, Al	1.2 %	1.2 %
Carbon, C	0.12 %	0.12 %
Chromium, Cr	24 %	24 %
Iron, Fe	74.68 %	74.68 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000102 ohm-cm	0.000102 ohm-cm

Processing Properties	Metric	English	Comments
Annealing Temperature	800 - 850 °C	1470 - 1560 °F	Cooling: forced air or water