SABIC Innovative Plastics Ultem DH1004F PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics Ultem DH1004F PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D 792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min <br>@Load 6.60 kg,<br> Temperature 337 °C |
10 g/10 min <br>@Load 14.6 lb,<br> Temperature 639 °F |
ASTM D 1238 |
| 14 g/10 min <br>@Load 5.00 kg,<br> Temperature 360 °C |
14 g/10 min <br>@Load 11.0 lb,<br> Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D 638 |
| 97.0 MPa | 14100 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 80 % | 80 % | 50 mm/min; ISO 527 |
| 85 % | 85 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.90 GPa | 421 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 136 MPa | 19700 psi | 2 mm/min; ISO 178 |
| 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 |
| 3.00 GPa | 435 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.700 J/cm <br>@Temperature 23.0 °C |
1.31 ft-lb/in <br>@Temperature 73.4 °F |
ASTM D 256 |
| 33.0 J/cm <br>@Thickness 3.20 mm |
61.8 ft-lb/in <br>@Thickness 0.126 in |
reverse notched; ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² <br>@Temperature 23.0 °C |
2.86 ft-lb/in² <br>@Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² <br>@Temperature -30.0 °C |
2.86 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB <br>@Temperature 23.0 °C |
NB <br>@Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB <br>@Temperature -30.0 °C |
NB <br>@Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 1.10 J/cm² <br>@Temperature 23.0 °C |
5.23 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179/2C |
| Impact Test | 88.0 J <br>@Temperature 23.0 °C |
64.9 ft-lb <br>@Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 88.0 J <br>@Temperature -20.0 °C |
64.9 ft-lb <br>@Temperature -4.00 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| 99.0 J <br>@Temperature 0.000 °C |
73.0 ft-lb <br>@Temperature 32.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C <br>@Temperature 23.0 - 150 °C |
27.8 µin/in-°F <br>@Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 56.0 µm/m-°C <br>@Temperature -20.0 - 150 °C |
31.1 µin/in-°F <br>@Temperature -4.00 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C <br>@Temperature 23.0 - 150 °C |
27.8 µin/in-°F <br>@Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C <br>@Temperature -20.0 - 150 °C |
30.6 µin/in-°F <br>@Temperature -4.00 - 302 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C 177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 214 °C <br>@Thickness 6.40 mm |
417 °F <br>@Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 204 °C <br>@Thickness 6.40 mm |
399 °F <br>@Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 | |
| 219 °C | 426 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | V-0 <br>@Thickness 0.750 mm |
V-0 <br>@Thickness 0.0295 in |
UL 94 |
| NBS Smoke Density | 0.70 <br>@Time 240 sec |
0.70 <br>@Time 0.0667 hour |
Flaming, Ds; ASTM E 662 |
| Oxygen Index | 46 % | 46 % | LOI; ASTM D 2863 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Instrumented Impact Ductility, 0°C, % | 100 | ASTM D 3763 |
| Instrumented Impact Ductility, -20°C, % | 90 | ASTM D 3763 |
| Instrumented Impact Ductility, 23°C, % | 100 | ASTM D 3763 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 20 A Linear Low Density Polyethylene
- Hyosung Topilene R601 PP
- LG Chemical AF360 ABS, TBBA-free Flame Retardant
- A. Schulman POLYFORT™ PP 7001
- 3M FM152 Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
- Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded
- Astaras Anviloy® Weld Rod
- Arkema Group Rilsan® BECN P20 TL Nylon 11 (Conditioned)
- Crucible Steel SIL 1 (JIS SUH1) Martensitic Steel
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved