- Lehmann & Voss LUVOCOM® 1850-8023 PBT, with carbon fiber
Lehmann & Voss LUVOCOM® 1850-8023 PBT, with carbon fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850-8023 PBT, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 105 MPa | 15200 psi | |
| Elongation at Yield | 2.3 % | 2.3 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |
| Flexural Strength | 155 MPa | 22500 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10 ohm | <= 10 ohm | |
| Insulation Resistance | <= 10 ohm | <= 10 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F7875 TPE, Fire Retardant
- Palm Labs Adhesives TURBO FUSE SERIES 130 CLEAR FLEXIBLE (100 Viscosity) Rapid Bonding Adhesive
- Quadrant EPP TIVAR® HPV UHMW-PE (ASTM Product Data Sheet)
- Polymer Resources PC-HM-FR1 Polycarbonate, 10% Glass Reinforced, Flame Retardant
- Imerys Kaolexâ„¢ SC Kaolin
- Solvay Specialty Polymers Catalyst PS/2LRO Polyolefin
- Silberline "L" Series L-228
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler
- C.O.I.M. LARIPUR® LPR5760 PTMG Polyether Polyurethane
- Fainplast Compounds KL 92 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved