SABIC Innovative Plastics Ultem 1010A PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port, China |
| Download PDF |
SABIC Innovative Plastics Ultem 1010A PEI.pdf
|
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D 792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation |
1.25 %
<br>@Temperature 23.0 °C
|
1.25 % <br>@Temperature 73.4 °F
|
ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0050
- 0.0070
cm/cm <br>@Thickness 3.20 mm
|
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
| Melt Flow |
17.8
g/10 min <br>@Load 6.60 kg,<br> Temperature 337 °C
|
17.8
g/10 min <br>@Load 14.6 lb,<br> Temperature 639 °F
|
ASTM D 1238 |
|
25
g/10 min <br>@Load 5.00 kg,<br> Temperature 360 °C
|
25
g/10 min <br>@Load 11.0 lb,<br> Temperature 680 °F
|
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D 638 |
| 60 % | 60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.59 GPa | 521 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched |
0.320
J/cm <br>@Temperature 23.0 °C
|
0.599
ft-lb/in <br>@Temperature 73.4 °F
|
ASTM D 256 |
|
0.350
J/cm <br>@Temperature -30.0 °C
|
0.656
ft-lb/in <br>@Temperature -22.0 °F
|
ASTM D 256 | |
| Izod Impact, Unnotched |
13.35
J/cm <br>@Temperature 23.0 °C
|
25.01
ft-lb/in <br>@Temperature 73.4 °F
|
ASTM D 4812 |
| Izod Impact, Notched (ISO) |
5.00
kJ/m² <br>@Temperature 23.0 °C
|
2.38
ft-lb/in² <br>@Temperature 73.4 °F
|
80*10*4; ISO 180/1A |
|
5.00
kJ/m² <br>@Temperature -30.0 °C
|
2.38
ft-lb/in² <br>@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) |
NB
<br>@Temperature 23.0 °C
|
NB <br>@Temperature 73.4 °F
|
80*10*4; ISO 180/1U |
|
NB
<br>@Temperature -30.0 °C
|
NB <br>@Temperature -22.0 °F
|
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched |
0.300
J/cm² <br>@Temperature 23.0 °C
|
1.43
ft-lb/in² <br>@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test |
33.0
J <br>@Temperature 23.0 °C
|
24.3
ft-lb <br>@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow |
50.0
µm/m-°C <br>@Temperature 23.0 - 150 °C
|
27.8
µin/in-°F <br>@Temperature 73.4 - 302 °F
|
ISO 11359-2 |
|
55.0
µm/m-°C <br>@Temperature -40.0 - 150 °C
|
30.6
µin/in-°F <br>@Temperature -40.0 - 302 °F
|
ASTM E 831 | |
| CTE, linear, Transverse to Flow |
50.0
µm/m-°C <br>@Temperature 23.0 - 150 °C
|
27.8
µin/in-°F <br>@Temperature 73.4 - 302 °F
|
ISO 11359-2 |
|
55.0
µm/m-°C <br>@Temperature -40.0 - 150 °C
|
30.6
µin/in-°F <br>@Temperature -40.0 - 302 °F
|
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) |
205
°C <br>@Thickness 3.20 mm
|
401
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
|
197
°C <br>@Thickness 3.20 mm
|
387
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 | |
| 219 °C | 426 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed:
- Polymax® Maxelast® P2635 TPE, PP Overmold or Standalone use
- Nilit Nilamon B3 H7 GK 35 15% Glass Fiber, 25% Mineral Reinforced PA6
- Nilit FRIANYL B63 GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- LNP Stat-Kon® PDX-S-90398 Polyamide 12, Stainless Steel Fiber (discontinued **)
- SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East)
- Elastocon TPE Technologies Elastocon® 8068N Thermoplastic Elastomer
- DuPont Performance Polymers Crastin® LW9020 BK580 PBT+ASA (Unverified Data**)
- Abatron AboCast 7802-1/AboCure 7804-4 (80 pbw) Epoxy
- EMS-Grivory Grivory® L 25 nat PA12