LATI Later 4E61 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer LATI
Trade Name Later
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4E61 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT). Toughened. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Linear Mold Shrinkage, Flow 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
Linear Mold Shrinkage, Transverse 0.018 - 0.0205 cm/cm
0.018 - 0.0205 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
>= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
>= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
>= 100 %

@Temperature 248 °F
Elongation at Yield 7.0 %
7.0 %
Tensile Modulus 0.180 GPa

@Temperature 120 °C
26.1 ksi

@Temperature 248 °F
0.300 GPa

@Temperature 90.0 °C
43.5 ksi

@Temperature 194 °F
0.600 GPa

@Temperature 60.0 °C
87.0 ksi

@Temperature 140 °F
1.90 GPa

@Temperature 23.0 °C
276 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
Charpy Impact, Notched 1.00 J/cm²

@Temperature -20.0 °C
4.76 ft-lb/in²

@Temperature -4.00 °F
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
284 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 230 - 245 °C
446 - 473 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa