SABIC Innovative Plastics ULTEM HU1110 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM HU1110 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable. UL94 V0 and 5VA listed.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Moisture Absorption 0.650 %
0.650 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.2 %
1.2 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 340 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 644 °F
 MVR [cm^3/10 min]; ISO 1133
21 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 21 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 145 MPa
21000 psi
ISO 2039-1
Tensile Strength, Yield 110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 60 %
60 %
5 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
Flexural Yield Strength 140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
210 °C
410 °F
Rate A/50; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 UL 94
Oxygen Index 47 %
47 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 IEC 60695-2-12
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2