Eastman 9663 PET (discontinued **)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman 9663 PET (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

VORIDIAN PET 9663 is a PET homopolymer widely used in the heatset industry and is FDA approved for food contact in hotfill applications. Voridian PET 9663 has a wide processing window and it’s versatility enables usage of this polymer in custom applications.Applications/UsesAutomotive parts containersFood packagingHousehold products containersPharmaceutical containersWine and liquor containersFood-contact containers

Physical Properties	Metric	English	Comments
Bulk Density	0.817 g/cc	0.0295 lb/in³	Poured; ASTM D1895
	0.881 g/cc	0.0318 lb/in³	Vibrated; ASTM D1895
Density	1.40 g/cc	0.0506 lb/in³	Crystalline Density; ASTM D1505
Melt Density	1.20 g/cc @Temperature 285 °C	0.0434 lb/in³ @Temperature 545 °F	ASTM D1238
Particle Size	2500 µm	2500 µm	Pellet Size
Viscosity Measurement	0.78 - 0.82	0.78 - 0.82	Intrinsic; VGAS-A-AN-G-V-1

Thermal Properties	Metric	English	Comments
Heat of Fusion	63.0 J/g	27.1 BTU/lb	ASTM E793
Specific Heat Capacity	1.10 J/g-°C	0.263 BTU/lb-°F	ASTM E1269
	1.30 J/g-°C @Temperature 80.0 °C	0.311 BTU/lb-°F @Temperature 176 °F	ASTM E1269
	1.40 J/g-°C @Temperature 100 °C	0.335 BTU/lb-°F @Temperature 212 °F	ASTM E1269
	1.90 J/g-°C @Temperature 200 °C	0.454 BTU/lb-°F @Temperature 392 °F	ASTM E1269
	2.10 J/g-°C @Temperature 280 °C	0.502 BTU/lb-°F @Temperature 536 °F	ASTM E1269
Melting Point	250 °C	482 °F	Crystalline Peak Melting Point; ASTM D3418

Descriptive Properties	Value	Comments
Acetaldehyde	<3ppm	VKCA-A-AS-G-GC-0001
Color, CIE a*	-2.0 ± 1.5	VGAS-A-AN-G-RS-001
Color, CIE b*	0.6 ± 1.5	VGAS-A-AN-G-RS-001
Color, CIE L*	78.5 min	VGAS-A-AN-G-RS-001
Fines, wt%, max	0.05	VGAS-A-AN-G-GA-1
Pellet Shape	Cubical