Shinkong Synthetic Fibers Shinite® D201G30 PBT, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® D201G30 PBT, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2204-30 CR-SX Fiberglass Reinforced SMC
- Resinlab® EP1325 Thixotropic, Heat Curing Epoxy Adhesive
- Loxim 130 01V0 Polycarbonate, 30% Glass Filled, Flame Retardant
- Daikin NEOFLON NF-2400 FEP Film
- ATI Allegheny Ludlum Stainless Steel Type 201L, 50% Cold Work (UNS S20103)
- Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C)
- Latrobe Lescalloy® Jethete M-152 ESR 6" RCS High Strength Stainless Steel
Copyright © lookpolymers.com All Rights Reserved