SABIC Innovative Plastics NORYL HIPS3190 HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics NORYL HIPS3190 HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complies with FDA Regulation 21 CFR 177.1640 for rubber modified polystyrene. HB rating from 0.062-0.125"" pending. Natural only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm <br>@Thickness 3.20 mm |
0.0060 - 0.0080 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.6 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 °C |
2.6 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | Type I, 5 mm/min; ASTM D638 |
| 24.0 MPa | 3480 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | Type I, 5 mm/min; ASTM D638 |
| 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 67 % | 67 % | Type I, 50 mm/min; ASTM D638 |
| 67 % | 67 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 5 mm/min; ASTM D638 |
| 2.21 GPa | 321 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 36.0 MPa | 5220 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.97 GPa | 286 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.13 GPa | 309 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.92 J/cm | 3.60 ft-lb/in | ASTM D256 |
| 0.740 J/cm <br>@Temperature -30.0 °C |
1.39 ft-lb/in <br>@Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 11.0 J <br>@Temperature -30.0 °C |
8.11 ft-lb <br>@Temperature -22.0 °F |
ASTM D3763 |
| 23.0 J <br>@Temperature 23.0 °C |
17.0 ft-lb <br>@Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.2 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C <br>@Thickness 3.20 mm |
194 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
| 93.0 °C <br>@Thickness 6.40 mm |
199 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C <br>@Thickness 3.20 mm |
171 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
| 83.0 °C <br>@Thickness 6.40 mm |
181 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 92.0 °C | 198 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB <br>@Thickness 1.52 mm |
HB <br>@Thickness 0.0598 in |
UL 94 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 99 GB 20 PP, 20% glass beads, mod. of mech. prop.
- Karina E 75/244-D-AT-IS-SI Clear PVC Compound
- Heatbath/Park Sta-Hard 45 Steel Brazing Neutral Salt
- Saint-Gobain Tygon® E-1000 Ultra-Soft Laboratory Tubing
- Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced
- Silon Taborex TA 2329 HD Catalyst Masterbatch
- DSM Stanyl® TE250F9 (DAM) Nylon 46 45% Glass Reinforced, Heat Stabilized, Flame Retardant (North America)
- Epoxyset Epoxibond EB-135 Unfilled Epoxy Adhesive
- CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Rolled Copper Alloy
Copyright © lookpolymers.com All Rights Reserved