- Aremco Ceramabond™ 890 High Temperature Ceramic Adhesive/Paste, Silicon Carbide Filled
Aremco Ceramabond™ 890 High Temperature Ceramic Adhesive/Paste, Silicon Carbide Filled
| Category | Ceramic , Carbide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 890 High Temperature Ceramic Adhesive/Paste, Silicon Carbide Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Thermal Conductivity Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Probes, Sensors
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 1.75 g/cc | 0.0614 - 0.0632 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 35000 - 55000 cP | 35000 - 55000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 54.2 J | 40.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.32 µm/m-°C | 2.40 µin/in-°F | |
| Maximum Service Temperature, Air | 1650 °C | 3000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 2.87 kV/mm | 73.0 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by <1 hour air set |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 2 | |
| 120 min @Temperature 371 °C |
2.00 hour @Temperature 700 °F |
Step 3 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | Blue-Gray | |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 890-T |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1512 Polypropylene Homopolymer, Fiber Spinning Grade
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 16% Plasticizer (discontinued **)
- LG Chemical HYPERIER IP1105 PA-PE Nanoclay Compound
- Ineos H02G-02 Polypropylene Homopolymer
- Sibur ABS 0809M Molding Grade ABS Plastic
- BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned)
- Beijing Evergrow Resources ACFP-200 Activated Carbon Fiber Powder
- Polystrand ThermoPro™ IE7015X X-Ply Cross-Ply Polypropylene-Glass Composite
Copyright © lookpolymers.com All Rights Reserved