SABIC Innovative Plastics ULTEM AUT195 PEI+PCE
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AUT195 PEI+PCE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.90 % | 0.90 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 24 g/10 min @Load 6.60 kg, Temperature 337 °C |
24 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 340 °C |
16 g/10 min @Load 11.0 lb, Temperature 644 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 |
| 3.17 GPa | 460 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 21.36 J/cm @Thickness 3.20 mm |
40.02 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 20.82 J/cm | 39.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 205 °C | 401 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Metallized Haze Onset | 195°C | SABIC Method |
Users viewing this material also viewed the following:
- Nye Lubricants 793 (NG) Synthetic Oil
- Parker Chomerics CHO-FORM 5519 Conductive Silicone
- G-9 Fiberglass Melamine Laminate Sheet
- Shin-Etsu Silicones X-52-854 Fluid
- Teknor Apex APEX® 280-NL Polyvinyl Chloride, Flexible
- Eastman Tenite Butyrate 580A3720016 Clear, Trsp Cellulose Acetate Butyrate
- BASF Ultramid® TG7S BK-102 35% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved