Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC SLC 2000 is a medium strength, low-cost, glass reinforced polyester compound with adjustable shrinkage. Ideal for circuit breakers, motor switch housings, fuse holders, brush holders, standoff insulators and conduit boxes. UL® recognized. This material was formerly known as Glastic® SLC 2000.
Physical Properties Metric English Comments
Specific Gravity 2.01 - 2.06 g/cc
2.01 - 2.06 g/cc
Water Absorption 0.070 - 0.12 %
0.070 - 0.12 %
24 hours, 23°C
Linear Mold Shrinkage 0.040 - 0.060 cm/cm
0.040 - 0.060 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 40 - 50
40 - 50
Tensile Strength, Ultimate 24.1 - 31.0 MPa
3500 - 4500 psi
Flexural Strength 89.6 - 96.5 MPa
13000 - 14000 psi
Flexural Modulus 12.8 - 13.6 GPa
1860 - 1970 ksi
Compressive Strength 138 - 152 MPa
20000 - 22000 psi
Izod Impact, Notched 2.67 - 3.20 J/cm
5.00 - 6.00 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Strength 10.9 kV/mm
278 kV/in
Short Time
Dissipation Factor 0.015

@Frequency 60 Hz
0.015

@Frequency 60 Hz
Condition D
0.017

@Frequency 60 Hz
0.017

@Frequency 60 Hz
Condition A
0.019

@Frequency 60 Hz
0.019

@Frequency 60 Hz
Condition A
Arc Resistance 185 sec
185 sec
Track Resistance >= 16.67 sec
>= 16.67 sec
Processing Properties Metric English Comments
Mold Temperature 138 - 166 °C
280 - 330 °F