Styrolution Styrolux T SBC
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Styrolution |
| Trade Name | Styrolux |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Styrolux T SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolux T is a new developmental, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux T has been developped for blending with a second SBC component, Styrolux S, which inceases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage).Excellent clarity and toughnessMaximum shrinkage up to 80%Very good shrinkage controlVery low gel contentInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption at Saturation | 0.070 % @Temperature 23.0 °C |
0.070 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | ISO 868 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Break | 250 % | 250 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
| Flexural Strength | 32.0 MPa | 4640 psi | ISO 178 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 46.0 °C @Load 5.10 kg |
115 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 62.0 °C @Load 1.02 kg |
144 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ASTM D 1003 |
| Transmission, Visible | >= 89 % @Wavelength 550 nm |
>= 89 % @Wavelength 550 nm |
ASTM D 1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 230 °C | 356 - 446 °F | ISO 294 |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
- Michelman® Resisto Coat™ PLUS Abrasion resistance coating
- Kraton® D1155 E (SBS) Liner Block Copolymer
- Indium Corp. In(OH)3 Crystalline Indium Hydroxide
- MetalTek MTEK 304L Cast UNS J92500 Austenitic Stainless Steel
- H.C. Starck Ampersint® AISI 316 L 31 µm For P/M, HIP/CIP, MIM
- Shakespeare WP-315 diameter 0.2 mm Weft Polyester Monofilament
- ChevronTexaco Rykon® 5W-20 Premium Oil MV
- Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin
- PolyOne Edgetek® PI-10GF/000 Polyetherimide (PEI), Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved