SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.
Physical Properties Metric English Comments
Specific Gravity 1.48 g/cc
1.48 g/cc
ASTM D792
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13.7 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 13.7 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 14 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
94.0 MPa
13600 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 80.0 MPa
11600 psi
5 mm/min; ISO 527
94.0 MPa
13600 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 5.30 GPa
769 ksi
1 mm/min; ISO 527
6.48 GPa
940 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 145 MPa
21000 psi
2 mm/min; ISO 178
156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 5.50 GPa
798 ksi
2 mm/min; ISO 178
5.58 GPa
809 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.390 J/cm
0.731 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.30 J/cm
6.18 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 15.0 J

@Temperature 23.0 °C
 11.1 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 32.0 µm/m-°C

@Temperature -40.0 - 150 °C
 17.8 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
32.0 µm/m-°C

@Temperature 23.0 - 150 °C
 17.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 35.0 µm/m-°C

@Temperature -40.0 - 150 °C
 19.4 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
35.0 µm/m-°C

@Temperature 23.0 - 150 °C
 19.4 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 204 °C
399 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
204 °C

@Thickness 3.20 mm
 399 °F

@Thickness 0.126 in
 unannealed; ASTM D648
206 °C

@Thickness 6.40 mm
 403 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 192 °C
378 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
199 °C

@Thickness 3.20 mm
 390 °F

@Thickness 0.126 in
 unannealed; ASTM D648
202 °C

@Thickness 6.40 mm
 396 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 211 °C
412 °F
Rate B/50; ISO 306
213 °C
415 °F
Rate B/120; ISO 306
216 °C
421 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 7.0 - 15 sec
7.0 - 15 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2