Star Plastics ABSFR1 Molding Grade ABSFR

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Star Plastics, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics ABSFR1 Molding Grade ABSFR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Maximum Moisture Content 0.15
0.15
Linear Mold Shrinkage 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.5 MPa
5300 psi
ASTM D638
Tensile Modulus 2.17 GPa
315 ksi
ASTM D638
Flexural Yield Strength 64.1 MPa
9300 psi
ASTM D790
Flexural Modulus 2.24 GPa
325 ksi
ASTM D790
Izod Impact, Notched 1.49 J/cm
2.80 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 75.6 °C
168 °F
unannealed, .125in; ASTM D648
Flammability, UL94 V-0
V-0
.062in
Processing Properties Metric English Comments
Rear Barrel Temperature 149 - 182 °C
300 - 360 °F
Middle Barrel Temperature 177 - 204 °C
350 - 400 °F
Front Barrel Temperature 191 - 232 °C
375 - 450 °F
Nozzle Temperature 191 - 232 °C
375 - 450 °F
Melt Temperature 191 - 232 °C
375 - 450 °F
Mold Temperature 48.9 - 76.7 °C
120 - 170 °F
Drying Temperature 76.7 - 87.8 °C
170 - 190 °F
Dry Time 2 - 4 hour
2 - 4 hour
Back Pressure 0.172 - 0.689 MPa
25.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm