SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 48 hrs @ 23°C, flow; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 48 hrs @ 23°C, xflow; SABIC Method |
| Melt Flow | 12 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
12 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | Type I, 50 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 50 mm/min, 1A; ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 50 mm/min; ASTM D638 |
| 3.3 % | 3.3 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527 |
| 6.58 GPa | 954 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 5.12 GPa | 743 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.60 GPa | 957 ksi | 2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D256 |
| Izod Impact, Unnotched | 5.68 J/cm | 10.6 ft-lb/in | 63.5*12.7*3.2mm, Cut; ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 10.0 kJ/m² <br>@Temperature -30.0 °C |
4.76 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 1.10 J/cm² <br>@Temperature -30.0 °C |
5.23 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Gardner Impact | 0.500 J | 0.369 ft-lb | ASTM D5420 |
| Dart Drop, Total Energy | 7.00 J <br>@Temperature 23.0 °C |
5.16 ft-lb <br>@Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C <br>@Temperature -30.0 - 100 °C |
2.78 µin/in-°F <br>@Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C <br>@Temperature -30.0 - 100 °C |
88.9 µin/in-°F <br>@Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 159 °C <br>@Thickness 3.20 mm |
318 °F <br>@Thickness 0.126 in |
ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 150 °C <br>@Thickness 3.20 mm |
302 °F <br>@Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 164 °C | 327 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6)
- Ineos Nova 731G High Impact Polystyrene (discontinued **)
- Overview of materials for PVC, Extruded
- Kennametal Stellite Delcrome 316 Iron Alloy
- Indium Corp. Indalloy 16 Low Melting Bismuth Alloy
- Shin-Etsu Silicones KM-907 Fluid
- Cosmic Plastics K66 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene
- Hexcel® HexPly® F593 Epoxy Resin, F3T584 Carbon Fabric
- SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved