- SABIC Innovative Plastics NORYL NH7112 PPE+HIPS
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH7112 PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to achieve UL94 flame ratings. This grade can be processed via extrusion or injection molding. Noryl NH7112 is available in custom colors and may be an excellent material candidate for use in electrical and electronics markets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.22 % | 0.22 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 300 °C |
14 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | Type I, 5 mm/min; ASTM D638 |
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 5 mm/min; ASTM D638 |
| 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 140 MPa | 20300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.75 GPa | 544 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.15 GPa | 602 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*3; ISO 180/1U | |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.10 J/cm² | 14.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.10 J/cm² @Temperature -30.0 °C |
14.8 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 550 µm/m-°C @Temperature -40.0 - 40.0 °C |
306 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 148 °C | 298 °F | Rate B/50; ASTM D1525 |
| 148 °C | 298 °F | Rate B/50; ISO 306 | |
| 150 °C | 302 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.00 mm |
V-1 @Thickness 0.0394 in |
UL 94 by SABIC-IP |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 3.00e+17 ohm | >= 3.00e+17 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.93 @Frequency 1.00e+6 Hz |
2.93 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 3.20 mm |
635 kV/in @Thickness 0.126 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0034 @Frequency 1.00e+6 Hz |
0.0034 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0034 @Frequency 1.00e+6 Hz |
0.0034 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Network Polymers Kepital® F30-03
- Polykemi AB POLYplex PMMA 500 Acrylic Glass
- Polimeri Europa SINKRAL B232/E ABS, Heat Stabilized (discontinued **)
- SABIC Innovative Plastics LNP STAT-LOY KX09024 ACETAL COPOLYMER (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS
- TriStar Ultracomp UC-400 Composite Bearing
- CTC SunPro® SP 200 TF 3033 Polypropylene Copolymer, 33% Talc Filled
- Eagle Brass 102 OF COPPER (Non-Certified), Hard
- ExxonMobil 524 Mobil SHC 500 Series
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.35 PHR Caytur 4
Copyright © lookpolymers.com All Rights Reserved